Polyvinylidene fluoride (PVDF)KF Polymer
KF Polymer‘s Line-up
We offer a diverse lineup of grades, ranging from low-molecular-weight homopolymers to high-molecular-weight polymers and copolymers. Based on molding and processing conditions as well as specific applications, we recommend a grade suited to meet your needs.
Properties (Units) |
Test method |
Conditions | Grade | ||||||
---|---|---|---|---|---|---|---|---|---|
#850 | #1000 | #1100 | #1300 | #1550 | #1700 | #2950 | |||
Type | - | - | Homopolymer | Copolymer | |||||
Features | - | - | Low MV | Low MV | Medium MV |
High MV, Higher Mechanical Properties |
High MV, Higher Mechanical Properties |
Ultra high MV, Higher Mechanical Properties |
Low MV, Low Elution Properties |
Main molding methods | Injection Molding & Extrusion |
Injection Molding & Extrusion |
Injection Molding & Extrusion |
Extrusion | Extrusion | Extrusion | Extrusion | ||
Examples of application | - | - | Valve, Pipe, Film |
Valve, Pipe, Film, Fiber |
Fitting, Film, Fiber |
Film, Fiber |
Membrane | - | Pipe, Tube |
Form | - | - | Powder, Pellet |
Powder, Pellet |
Powder, Pellet |
Powder, Pellet |
Powder | Powder | Pellet |
Melting point (℃) |
ASTM D3418 |
173 | 173 | 173 | 173 | 173 | 173 | 172 | |
Melt flow rate (g/10min) |
ASTM D1238 |
230℃,5kg | 15-30 | 5-8 | 2-4 | 0.8-1.4 | - | - | 4-8 |
230℃,21.6kg | - | - | - | 11.2 | 3.8 | 1.7 | - |
Physical Properties
Properties (Units) |
Test method |
Conditions | Grade | ||||||
---|---|---|---|---|---|---|---|---|---|
#850 | #1000 | #1100 | #1300 | #1550 | #1700 | #2950 | |||
Specific gravity (g/cm3) |
ASTM D792 |
- | 1.77 - 1.79 | ||||||
Inherent viscosity (dl/g) |
ISO 1628-1 |
30℃,DMF | 0.85 | 1 | 1.1 | 1.3 | 1.5 | 1.7 | 1.05 |
Refractive index | ASTM D542 |
25℃ | 1.42 | ||||||
Water absorption (%) |
ASTM D570 |
23℃ | 0.03 | ||||||
Melt viscosity (Pa・s) |
ASTM D3835 |
240℃,50sec-1 | 1200 | 2200 | 3300 | 5000 | - | - | 2700 |
260℃,50sec-1 | - | - | 2500 | 4500 | 6500 | 8500 | - | ||
Melt flow rate (g/10min) |
ASTM D1238 |
230℃,5kg | 15-30 | 5-8 | 2-4 | 0.8-1.4 | - | - | 4-8 |
230℃,21.6kg | - | - | - | 11.2 | 3.8 | 1.7 | - |
Thermal Properties
Properties (Units) |
Test method |
Conditions | Grade | ||||||
---|---|---|---|---|---|---|---|---|---|
#850 | #1000 | #1100 | #1300 | #1550 | #1700 | #2950 | |||
Melting point (℃) |
ASTM D3418 |
173 | 173 | 173 | 173 | 173 | 173 | 172 | |
Crystallization point (℃) |
ASTM D3418 |
140 | |||||||
Glass transition point (℃) |
DMA method | -35 | |||||||
Glass transition point (℃) |
ASTM D746 |
-13 | -31 | -37 | -47 | - | - | -30 | |
Vicat softening temperature (℃) |
ISO 306 |
50℃/h,10N | 171 | 172 | 172 | 173 | - | - | 166 |
Coefficient of linear expansion (10-4K-1) |
ISO 11359-2 |
RT-80℃ | 1.6 | ||||||
Thermal conductivity (W/m・K) |
ASTME 1530 |
23℃ | 0.17 | ||||||
Specific heat capacity (J/g・K) |
JIS K7123 |
23℃ | 1.2 |
Mechanical Properties
Properties (Units) |
Test method |
Conditions | Grade | ||||||
---|---|---|---|---|---|---|---|---|---|
#850 | #1000 | #1100 | #1300 | #1550 | #1700 | #2950 | |||
Izod impact strength (kJ/m2) |
ASTM D256 V-notched (ISO180) |
20℃ | 7.9 | 15 | 33 | 77 | - | - | 14 |
0℃ | 5 | 9.7 | 13.3 | 37 | - | - | 8.2 | ||
-20℃ | 3 | 3 | 3.4 | 11.5 | - | - | 3 | ||
-40℃ | 3 | 2.7 | 2.9 | 3.6 | - | - | 2.8 | ||
Shore hardness (D) |
ISO 868 |
23℃,50N | 78 | 78 | 79 | 78 | - | - | 77 |
Tensile strength at yield (MPa) |
ISO 527-2 |
57 | 57 | 59 | 67 | - | - | 54 | |
Tensile elongation at break (%) |
ISO 527-2 |
76 | 28 | 36 | 25 | - | - | 29 | |
Tensile modulus (MPa) |
ISO 527-2 |
2510 | 2330 | 2430 | 2580 | - | - | 2120 | |
Flexural strength (MPa) |
ISO 178 |
75 | 74 | 71 | 70 | - | - | 67 | |
Flexural modulus (MPa) |
ISO 178 |
1990 | 1570 | 1500 | 1870 | - | - | 1760 | |
Compressive strength (MPa) |
ISO 604 |
76 | 74 | 71 | 68 | - | - | 65 | |
Compressive modulus (MPa) |
ISO 604 |
1700 | 1570 | 1500 | 2020 | - | - | 1770 | |
Abrasion resistance (10-6kg) |
Taber CS-17 |
1kg,1000rev | 31 | 31 | 31 | 31 | - | - | 32 |
Electrical Properties
Properties (Units) |
Test method |
Conditions | Grade | ||||||
---|---|---|---|---|---|---|---|---|---|
#850 | #1000 | #1100 | #1300 | #1550 | #1700 | #2950 | |||
Volume resistivity (Ωcm) |
ASTM D257 |
DC1kV | 1014-15 | ||||||
Surface resistance (Ω/□) |
ASTM D257 |
DC500V | >1015 | ||||||
Breakdown strength (MV/m) |
ASTM D149 |
Thickness: 34μm | 300 | ||||||
Dielectric constant | ASTM D150 |
1kHz | 10 | 10 | 10 | 10 | - | - | 10 |
Dissipation factor | ASTM D150 |
1kHz | 0.015 | 0.015 | 0.015 | 0.015 | - | - | 0.02 |
Flame Resistance
Properties (Units) |
Test method |
Conditions | Grade | ||||||
---|---|---|---|---|---|---|---|---|---|
#850 | #1000 | #1100 | #1300 | #1550 | #1700 | #2950 | |||
Burning rate | UL94 | V-0 equivalent | V-0 | V-0 equivalent | V-0 | V-0 equivalent | V-0 equivalent | V-0 equivalent | |
Limiting oxygen index (%) |
ISO 4589-2 |
TYPE-IV | 44 |
The product names include a raw material form code at the beginning of the grade name. Powder grade: W, Pellet grade: T.
Learn more about KF Polymer
Download Brochure
Download Brochure
Download SDS
Contact for Inquiries
KF Products Department
For inquiries regarding the following products,
please contact the site below.
please contact the site below.
- Product Groups
- Search by Application
-
Advanced Materials
-
Polyphenylene sulfide (PPS)
- Fortron KPS
-
Polyvinylidene fluoride (PVDF)
- KF Polymer
- KF Piezo
-
Carbon Products
- KRECA Carbon Fiber
- BAC
-
Polyglycolic acid (PGA)
- Kuredux
-
Microsphere
- KUREHA Microsphere
-
-
Specialty Chemicals
-
Pharmaceuticals
- KREMEZIN / COVALZIN
-
Agrochemicals
- Metconazole
- Ipconazole
-
Industrial Chemicals
- Inorganic Chemicals
- Organic Chemicals
-
-
Specialty Plastics
-
Household Products
- NEW Krewrap
- Kichinto-San Series
-
Commercial-use food packaging materials
-
Krehalon Film /
Kureha Auto Packer (KAP)
-
Fishing Lines
- SEAGUAR
-
- Construction & Other Services